Microstructure and mechanical properties of B4C matrix composites prepared via hot-pressing sintering with Pr6O11 as additive

High-performance B₄C-PrB₆ composites were prepared via hot-pressing sintering with matrix phase B₄C and with 2–5 wt% Pr₆O₁₁ as additive. The effects of different sintering processes and Pr₆O₁₁ content on the microstructure and mechanical properties of the composites were studied in detail. It is found that increasing sintering temperature and pressure will contribute to the densification of B₄C-PrB₆ composites. Coarse grains are formed in B₄C without additives at high temperature conditions, resulting in the decrease of the densification. Pr₆O₁₁ can effectively hinder the formation of coarse grains and finally promote the densification of the composites. The main toughening mechanisms of composites was crack deflection. The composites with 4 wt% Pr₆O₁₁ prepared at 2050 °C and 25 MPa had the best comprehensive mechanical properties. The relative density, hardness, flexural strength and fracture toughness reached to 98.9%, 37.6 GPa, 339 MPa and 4.4 MP am^1/2, respectively.     

Dielectric properties of alumino-silicate ceramics synthesized by plasma sintering

The polycrystalline ceramic specimens of three different alumino-silicate solid solutions (Al_0.70Si_0.30O, Al_0.73Si_0.27O and Al_0.75Si_0.25O) consisting of different alumina and silica concentrations have been synthesized by thermal plasma sintering technique. From structural analysis carried out by X-ray diffraction, the ceramics are mostly found to consist of two different phases of mullite and sillimanite. SEM images of these ceramics reveal a high dense and less porous microstructure with homogeneous distribution of grains throughout their surface. These materials exhibit high dielectric constant value (>10³) with low dissipation factor. The AC conductivity analysis reveals that Al_0.70Si_0.30O and Al_0.75Si_0.25O ceramics possess room temperature conductivity values of the order of 10^?5, whereas Al_0.73Si_0.27O has conductivity of 10^?7 order that increases with rise in temperature. From the Nyquist plots, the grain and grain boundary conductivities are distinguished and negative temperature coefficient of resistance behavior is identified in these ceramics with small positive temperature coefficient of resistance effect.     

SnO2 modified PNN-PZT ceramics with ultra-high piezoelectric and dielectric properties

In this work, a two-step solid-state reaction method is used to prepare the 0.55 Pb(Ni_1/3Nb_2/3)O₃-0.135PbZrO₃-0.315PbTiO₃/xSnO₂ (PNN-PZT/xSnO₂) ceramics. The influences of SnO₂ on the crystalline structure, electromechanical properties, and temperature stability of PNN-PZT ceramics were studied in detail. The results demonstrate that the Sn⁴⁺ ions are successfully introduced into the PNN-PZT crystalline lattice and substitute B-site Ni²⁺ and Zr⁴⁺. The x = 0.0025 ceramic with the coexistence of rhombohedral, tetragonal, and pseudocubic phases exhibits the optimized comprehensive properties: the quasi-static piezoelectric constant d₃₃, large-signal d₃₃*, electromechanical coupling coefficients k_p and k_t, free dielectric constant ε_r, and mechanical quality factor Q_m are 1123 pC/N, 1250 p.m./V, 0.63, 0.54, 9529, and 57, respectively. Meanwhile, the Curie temperature for this composition is 103 °C, almost maintaining the same level as the PNN-PZT matrix. After annealing at 75 °C, the retained d₃₃ of x = 0.0025 ceramic is as high as 975 pC/N, superior to the PNN-PZT matrix (retained d₃₃ ≈ 873 pC/N). Our results provide a promising piezoelectric material for board bandwidth, high sensitivity, and miniaturized medical ultrasonic transducers applications.     

Design,synthesis, structure,and stability of novel multi-principal element (Ti,Zr,Hf,W)C ceramic with a miscibility gap

Here we design a novel multi-principal element carbide system (Ti,Zr,Hf,W)C with a miscibility gap using computational tools and report on the formation of a single-phase (Ti,Zr,Hf,W)C after spark plasma sintering. The (Ti,Zr,Hf,W)C shows high nanohardness (32.7 GPa) and fracture toughness (5 MPa·m^1/2). Aging studies at 1350 °C for 100 h show that the single-phase carbide solid solution is quite stable even though this temperature is within the predicted miscibility gap of the system. Detailed electron microscopy characterization shows that phase separation has initiated with minor decomposition after aging by forming rock-salt (Ti,W)C- and (Zr,Hf)C-rich phases as well as hexagonal WC precipitates. We show that the (Ti,W)C- and (Zr,Hf)C-rich phases form a lamellar structure upon aging and the interlamellar spacing is considerably coarser than what has been previously found for the binary (Ti,Zr)C system. The decomposition kinetics, on the other hand, is sluggish due to the reduced driving force for phase decomposition.     

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

SiC composite ceramics have good mechanical properties. In this study, the effect of temperature on the microstructure and mechanical properties of SiC–TiB₂ composite ceramics by solid-phase spark plasma sintering (SPS) was investigated. SiC–TiB₂ composite ceramics were prepared by SPS method with graphite powder as sintering additive and kept at 1700 °C, 1750 °C, 1800 °C and 50 MPa for 10min.The experimental results show that the proper TiB₂ addition can obviously increase the mechanical properties of SiC–TiB₂ composite ceramics. Higher sintering temperature results in the aggregation and growth of second-phase TiB₂ grains, which decreases the mechanical properties of SiC–TiB₂ composite ceramics. Good mechanical properties were obtained at 1750 °C, with a density of 97.3%, Vickers hardness of 26.68 GPa, bending strength of 380 MPa and fracture toughness of 5.16 MPa m^1/2.     

Anisotropic thermal expansion and ionic conductivity of a crystal-oriented,Mg2+-conducting NASICON-type solid electrolyte

Multivalent ion-conducting ceramics are required for the manufacture of high-safety, high-capacity rechargeable batteries. However, the low ionic conductivity of solid electrolytes and discrepancies in the thermal expansion between the battery components limit their widespread application. Furthermore, anisotropic thermal expansion in crystals during battery manufacturing and the charge-discharge cycles causes the formation of microcracks, which degrade the battery performance. The physical properties of ceramic materials with anisotropic crystal structures can be modified by varying the crystallographic orientation of their grains. In this study, a co-precipitation approach was used to synthesize an Mg²⁺-conducting (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ solid electrolyte, and the grain orientation in the bulk sample was controlled using strong magnetic fields during the slip casting process. The results showed that inducing an orientation along the c-axis enhanced the apparent ionic conductivity of the bulk sample. It was also observed that (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ crystal has a negative volumetric thermal expansion despite a positive linear thermal expansion along its c-axis. By adjusting the c-axis orientation of the grains, (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ electrolytes with negative or positive linear thermal expansion coefficient have been produced. The findings of this study suggest that solid-electrolytes with negative, positive, or zero linear thermal expansion can be produced to create more compatible and higher-performance solid-state devices.     

Corrosion behaviour of an industrial shot-peened and coated automotive spring steel AISI 9254

A high-strength low-alloy steel, AISI 9254 (54SiCr6), is widely used for suspension spring production in the automotive industry. In this work, industrially manufactured zinc phosphate coated helical springs are subjected to detailed microstructural and surface analysis for better understanding of corrosion evolution. The material’s free corrosion potential and anodic/cathodic behaviour were investigated in NaCl solutions and corrosion propagation mechanisms were studied using potentiostatic polarisation on cross-sectional and external surfaces. The bulk material is fully martensite with uniformly distributed MnS inclusions, while the spring surface has a 2–3?μm mechanically deformed region introduced by shot-peening and a thin zinc phosphate coating. The corrosion open circuit potential of bulk material and shot-peened spring surface was about –0.7V_SCE without significant difference, while phosphated surface is more noble (more positive potential). MnS inclusions, stimulating the anodic attack in the steel, influence corrosion propagation and pit morphology to a large extent that can have an impact on the spring performance.     

Investigation of structural,optical, electrical,and magnetic properties of Fe-doped La0.7Sr0.3MnO3 manganites

In this work, the physical properties of nanocrystalline samples of La_0.7Sr_0.3Mn_1−xFe_xO₃ (0.0 ≤ x ≤ 0.20) perovskite manganites synthesized by the reverse micelle (RM) technique were explored in detail. The phase purity, crystal structure, and crystallite size of the samples were determined using X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. All the samples had rhombohedral crystal structure and crystallite size increased with increase in Fe content in La_0.7Sr_0.3MnO₃. The scanning electron micrographs (SEMs) exhibited smooth surface morphology and nonuniform shape of the particles. The optical properties studied using UV-visible absorption spectroscopy revealed a decrease in the absorbance and optical band gap with an increase in Fe content in La_0.7Sr_0.3MnO₃ compound. The temperature-dependent resistivity measurements revealed semiconducting nature of x = 0 and 0.1 samples up to the studied temperature range, while a metal-to-insulator transition was observed at higher Fe doping. Magnetic studies revealed weak ferromagnetism in all the samples and a reduction in the maximum magnetization with an increase in Fe content. A close correlation between electrical transport and magnetic properties was observed with the doping of Fe ion in La_0.7Sr_0.3MnO₃ at Mn site. These results advocate strong interactions associated with the double exchange mechanism among Fe³⁺ and Mn³⁺ ions.     

Viscoelastic Behavior of Synthesized Liquid Soaps and Surface Activity Properties of Surfactants

In the present work, a rheological study of liquid soaps prepared from different mixture of surfactants as a function of surfactant type and concentration was performed. The curves of shear stress vs. shear rate and viscosity vs. shear rate were recorded at constant temperature, 294 ± 0.1 K. The surface activity properties were also studied. The results of the study showed that values of surface tension, γ, were in the range 31–40 mN m⁻¹ and the critical micelle concentration (CMC), was of the order 10⁻⁴ mol L⁻¹. The calculated maximum surface excess, Γ_max, varied from 2.40 to 3.66 μmol m⁻², while minimum area per molecule, A_min, varied from 41.1 (for amphoterics) to 81.4 Ų (for nonionic surfactants). The standard free energy of micellization, −29.8 and −29.3 kJ mol⁻¹ for anionic and amphoteric surfactants, respectively, were while values for nonionic surfactants varied between −31.8 and − 30.3 kJ mol⁻¹. The free energy of adsorption, was the lowest for amphoteric surfactants (−37.9 kJ mol⁻¹), followed by anionics (−40.4 kJ mol⁻¹) and nonionics (−43.34 to −46.84 kJ mol⁻¹), indicating that micellization process is spontaneous in the examined medium. The synthetized liquid soaps show pseudoplastic behavior and they achieved pipe flow. The results of this research indicate that flow behavior was affected significantly by the ionic charge of the surfactant and the ionic strength of the formulation, suggesting that the flow behavior could be changed by manipulating the choice of the surfactant and salinity. The pH value of all liquid soaps examined were weakly acidic, in the range of 5.0–6.4.     

等温退火对8030铝合金导线组织性能的影响

研究了不同等温退火工艺对8030铝合金导线组织及性能的影响。结果表明:等温退火前后合金均由α-Al基体和Al₆Fe相组成。在同一等温温度下,随着等温时间的延长组织逐渐趋于均匀化;同一等温时间下,随着等温温度的升高,组织趋于均匀化的时间缩短。经过等温退火处理后铝合金导线的导电率均有所提高,在470 ℃均匀化退火24 h后再经240 ℃等温4 h,合金导电率达到最高值57.21%IACS,比未经热处理试样的导电率提高了2.4%IACS。经过等温退火处理后铝合金导线的硬度及抗拉强度均有所降低,塑性大幅度提高。在470 ℃均匀化退火24 h后再经260 ℃等温8 h,合金的伸长率最高可达23.64%。热处理前后合金均为塑性断裂。